410 Stainless Steel

410 stainless steel

Stainless steel 410 is a basic martensitic grade which contains 11.5% chromium, offering both exceptional wear and corrosion resistance. SS 410 is corrosion resistant to some chemicals, food, mild acids, water, and air. It also proves adequate resistance to nitric acid, concentrated sulfuric acid, dilute acetic acid and naphtha. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it's hardened and tempered. 

410 stainless steel is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more. 410 SS is generally used for applications which involve mild corrosion, high strength, and heat resistance.  Please contact Best Stainless for more information about 410 SS, its properties, and its applications.

Heat Treatment:

Galvanizing: Heat slowly to 1500 -1650°F, cool to 1100°F in furnace, air cool. Process Galvanizing: Heat to 1350 -1450°F, air cool. Hardening: Heat to 1700 - 1850°F, air cool or oil quench. Follow by temper or stress-relief. Stress Relieving: Heat at 300 - 800°F for 1 to 2 hours, air cool. See our stainless steel heat treating services.

Forming:

410 SS has cold working properties which allow it to be temperately drawn and shaped in the galvanized condition.

Fabrication:

The martensitic alloys offer unique hardening capabilities which limit their capability of being welded using conventional techniques. 410 stainless steel must first be pre-heated, followed by a post-weld galvanizing treatment to alleviate cracking.

410 SS Standards

  • UNS S41000
  • ASTM A182
  • ASTM A276
  • ASTM A479

Composition (%)

  • Carbon 0.080-0.150
  • Chromium 11.50-13.50
  • Manganese 1.0 Max
  • Phosphorus 1.0 Max
  • Silicon 1.00 Max
  • Sulfur 0.030 Max

Applications

  • Pump Shafts
  • Valve Components
  • Gas and Steam Turbine Components

410 SS Bar Stock

 

410 Stainless Steel Mechanical Properties

Material Type Condition Ultimate Tensile Strength (PSI) 0.2% Yield Strength (PSI) Elongation (% In 2in.) Reduction Of Area (%) Hardness Brinell Hardness Rockwell
410 SS
T 100,000 80,000 12 40 * *
  H 120,000 90,000 12 40 * *
  Annealed 70,000 40,000 16 45 * *
  Class2 110,000 85,000 15 45 269 Max *
  NACE MRO 175 * * * * * 22 HRC Max